Product model: PFEBS61D553
Product description: This product is made of high-purity polypropylene resin as the base material, adding high-quality and efficient flame retardants, antioxidants and other processing aids, and is made by mixing, plasticizing and granulating. It has excellent mechanical and physical properties, electrical properties, flame retardant properties, and has high heat resistance and other characteristics. No precipitation pollution, in line with the relevant requirements of Rohs, etc., easy to extrude and process.
Product application: Suitable for the production of 0.35mm²~6mm² automotive cables required by ISO19642/ISO 6722/JASO D611 and other standards.
| NO. | Testing items | VALUE | Typicalvalue | UNIT | Metho d |
| 1 | Density（20℃） | ≤1.2 | 1.15 | g/cm3 | GB/T 1033 |
| 2 | Tensile strength | ≥10 | 12.9 | MPa | GB/T 1040.2 |
| 3 | Elongation at break | ≥150 | 180 | ％ | GB/T 1040.2 |
| 4 | Impact brittlement temperature（-40 ºC) | ≤15/30 | 0/30 | 个 | GB/T 5470 |
| 5 | Volume resistivity(20ºC) | ≥1.0×1011 | 4.5×1011 | Ω·m | GB/T 1410 |
| 6 | /Dielectric strength(20ºC) | ≥20 | 25 | MV/m | GB/T 1408.1 |
| 7 | heat deterioration 150℃，240h | ||||
| After winding, the conductor is not exposed visually, and the 1kV voltage is applied for 1min without breakdown | ISO6722 | ||||
| 8 | /heat deterioration 125℃，3000h | ||||
| After winding, the conductor is not exposed visually, and the 1kV voltage is applied for 1min without breakdown | ISO6722 | ||||
| 9 | Thermal overload 175℃，6h | ||||
| After winding, the conductor is not exposed visually, and the 1kV voltage is applied for 1min without breakdown | ISO6722 | ||||
| 10 | Heat shrink 150℃，15min | ||||
| The maximum shrinkage of insulation at any end | ISO6722 | ||||
| should not exceed 2mm | |||||
| 11 | Solvent resistance (outer diameter rate of change) | ||||
| Gasoline resistance (ISO1817C, 23°C, 20h)h | |||||
| Rate of change of outer diameter | ≤15 | 12.6 | % | GB/T25087/ISO14572 | |
| Diesel resistance (90%ISO1817 3# oil + 10% paraxylene, 23°C, 20h) | |||||
| Rate of change of outer diameter | ≤15 | 2.3 | % | GB/T25087/ISO14572 | |
| Engine oil resistance (ISO1817 2# oil, 50°C, 20h) | |||||
| Rate of change of outer diameter | ≤15 | 3.1 | % | GB/T25087/ISO14572 | |
| 12 | Ozone resistance, ozone concentration (volume ratio)（250~300）×10-6%,25℃, 24h | ||||
| Visually does not crack | |||||
| 13 | Resistant to hot water，85℃, 168h,10%NaCl，循环5次/Cycle 5 times | ||||
| Insulation volume resistivity≥109Ω.mm | ISO6722 | ||||
| No cracking visually, no breakdown when applying 1kV voltage for 1min | |||||
| 14 | Alternating damp heat, cycle 8h, 150°C, humidity 80-100, 40 cycles | ||||
| After unfolding, the conductor is not exposed visually, and a voltage of 1kV is applied for 1min without breakdown | ISO6722 | ||||
| 15 | Flame retardant | The flame is extinguished within 30s, and at least 50mm of the end of the specimen should be left unburned | ISO6722 | ||
| 16 | Grinding | Meets ISO 19642 requirements for the number of grindings | |||
| 17 | Scraping | Meets ISO 19642 requirements for scraping cycles | |||
| 18 | Hardness | 61±3 | 61 | D | GB/T2411 |