Halogen-Free irradiated Cross-linked Polyethylene Cable Material

Halogen-Free irradiated Cross-linked Polyethylene Cable Material has excellent mechanical and electrical properties, wide processing temperature margin, etc.

Product application: Suitable for the production of insulation layers of various cables.

Testing items	Value	Typical Value	Unit	Method
Density	0.98±0.03	0.98	g/cm3	GB/T1033
Tensile strength	≥10	14.5	MPa	GB/T1040.2
Elongation at break	≥200	340	％	GB/T1040.2
Hot Extension 200℃ 0.2Mpa 15min
Elongation under load	≤175	90	％	GB/T2951.21
Permanent change rate after cooling	≤15	2	％
Heat Deterioration 175±2℃ 240H
Change rate of tensile strength	≤±30	12	%	GB/T2951.12
Change rate of elongation at break	≤±30	-10	%	GB/T2951.12
Impact brittle temperature	≤15/30	0/30	Pcs	GB/T5470
Volume resistivity (20ºC)	≥1.0×10^13	1.5×10^13	Ω·m	GB/T1410
Volume resistivity (20ºC)	≥1.0×10^10	2.5×10^10	Ω·m	GB/T1410
Dielectric strength (20ºC)	≥20	40	MV/m	GB/T1408.1
Resistant to Damp Heat 90℃
Relative Humidity 85% 1000H
Change rate of tensile strength	≤-30	-18	%	EN60068-2-78
Change rate of elongation at break	≤-30	-19	%	EN60068-2-78
Amount of HCl and HBr Gas released	≤2	0	mg/g	GB/T17650
PH value of combustion gas	≥4.3	5.8	/	GB/T17650
Electrical conductivity of combustion gas	≤10	5	μs/mm	GB/T17650
Hardness	96±3	96	15A	GB/T2411

Notes:

1. After the extruder temperature reaches the set value before starting the machine, it needs to be kept constant for about 0.5 hours.

2. When starting the machine to discharge, the melt temperature should be controlled at about 160-170°C.

3. The recommended filter selection is a 60 mesh + 80 mesh + 60 mesh combination filter.

Next Product Inquiry

ARE YOU INTERESTED IN OUR PRODUCT?

Why Don't You Contact Us

Products

125℃ Radiation XLPO-HFFR For Automotive Wire

This product is made of high-purity polyolefin resin as the base material, adding high-quality and efficient flame retardants, cross-linking sensitizers, antioxidants and other processing aids, and is made through mixing, plasticizing and granulation. It has excellent mechanical and physical properties, electrical properties, flame retardant proper

Learn More

150℃ Radiation XLPO-HFFR For Automotive Wire

Its basic parameters and application fields are introduced. It has excellent mechanical and physical properties, electrical properties and flame retardant properties, and is highly heat-resistant, pollution-free, meets environmental protection standards, and is easy to process. It is especially suitable for high-voltage/low-voltage wires and cables

Learn More

Application

TPU new energy vehicle charging pile cable material

TPE New Energy Vehicle Charging Pile Cable Material

XLPE Charging Pile Cable Insulation Material

125℃ VW-1 Energy Sorage Battery Cable Material

EN Locomotive Wire And Cable Sheath Material

National Standard Locomotive Wire And Cable Sheath Material

TPU new energy vehicle charging pile cable material

80℃ TPU charging pile cable sheath material is made of polyether polyurethane elastomer as the base material and mixed with other additives by extrusion and granulation. It is suitable for charging pile charging cables.

TPE New Energy Vehicle Charging Pile Cable Material

TPE charging pile sheath material uses high-purity resin as the base material, adds halogen-free flame retardants, antioxidants, etc., and is mixed and extruded into granules. It is commonly used for the outer sheath and insulation of charging pile chargi

XLPE Charging Pile Cable Insulation Material

This product is mainly made of XLPE material and is suitable for charging pile insulation cables in accordance with GB/T33594, EN50620 and other standards.

125℃ VW-1 Energy Sorage Battery Cable Material

125℃-UL94-VW1-XLPO energy storage battery connecting wire material is a new type of halogen-free flame retardant environmentally friendly material, suitable for all kinds of energy storage battery connecting wires.

EN Locomotive Wire And Cable Sheath Material

European standard cross-linked polyolefin high-speed rail locomotive wire and cable sheath material is mainly used for cables for high-speed rail, subway, train and other locomotives. This page mainly introduces its main parameters.

National Standard Locomotive Wire And Cable Sheath Material

The national standard high-speed rail locomotive cable sheath material is mainly used for various types of locomotive cables of Chinese standards, such as CRH series high-speed rail. This page mainly displays its basic parameters and application areas.

News/Blog

Angreen | Manufacturer of modified plastic cable granular materials

Jul. 02, 2024

Angreen Advanced Material Technology Co., Ltd., a high-tech enterprise in China, specializes in eco-friendly wire and cable materials, including LSZH, XLPE, TPU, TPE, and silicone. With cutting-edge R&D, global certifications, and applications in EVs, 5G, and more, Angreen leads innovation in polymer solutions.

Angreen helps the 2024 Asia Cable Exhibition to be held successfully

Jul. 09, 2024

From June 26 to June 28, 2024, the 2024 Asian Wire and Cable Industry Exhibition was officially launched at the China Import and Export Fair Complex in Guangzhou, and the 2024 Asian Wire and Cable Industry Exhibition Summit Forum series of activities were held.

TPU/TPE charging pile cable sheath and insulation material

Jul. 16, 2024

In the tide of global energy transformation, the new energy vehicle industry has ushered in unprecedented development opportunities. In 2023, the Chinese automobile market will set a new record with a production of 30.161 million vehicles and a sales volume of 30.094 million vehicles.