Silane cross-linked LSZH polyolefin material for household wiring

Silane cross-linked low smoke halogen-free polyolefin material

Product Description:

This product complies with RoHS, REACH and other relevant environmental protection requirements, and the material properties meet the standard requirements of JB/T 10436-2004. The product has excellent processing performance and a faster cross-linking speed.

Application Area:

Suitable for wiring wires for construction.

Category	Application
105℃	Suitable for extrusion, 6 square meters and below can be bundled A and B
105℃	Suitable for extrusion tubes, 6 square meters and below can be bundled A and B
105℃	Suitable for extrusion, 6 square meters and below can be bundled A, B and C
125℃	Suitable for extrusion, 6 square meters and below can be bundled A and B
125℃	Suitable for extrusion tubes, 6 square meters and below can be bundled A and B
125℃	Suitable for extrusion, 6 square meters and below can be bundled A, B and C

Product Parameters

Test items		UNIT	Typicalvalue
Test items		UNIT	PFXBS95461	PFXBS95462	PFXBS95463	PFXBS95464	PFXBS95465	PFXBS95466
Appearance		-	conform to	conform to	conform to	conform to	conform to	conform to
Original tensile strength		MPa	13.5	13.5	12.5	13.5	13.5	12.5
Original elongation at break		%	185	185	180	185	185	180
Heat aging	Test conditions	-	136℃*168h			158℃*168h
	Tensile strength retention rate	%	20	20	15	20	20	15
	Elongation at break retention rate	%	-15	-15	-10	-15	-15	-10
Low temperature shock	Test conditions	-	-40℃
Low temperature shock	Number of failures (≤15/30)	PCS	0	0	0	0	0	0
Oxygen index		%	33	33	38	33	33	33
Volume resistivity (20°C)		Ω.m	2*1012	1*1012	2*1012	2*1012	2*1012	1*1012
Dielectric strength (20°C)		MV/m	28	28	25	28	28	25
Thermal stretching	Test conditions	-	200ºC\0.2MPa\15min
	Elongation under load	%	35	35	30	35	35	30
	Permanent change rate after cooling	%	0	0	0	0	0	0
PH		-	4.9	4.9	4.9	4.9	4.9	4.9
Conductivity		μs/mm	0.61	0.61	0.61	0.61	0.61	0.61
Smoke Density: Flame		Ds max	90	90	80	90	90	80

The use of silane cross-linked low-smoke halogen-free polyolefin materials for household wires is a safe and environmentally friendly choice.

This material has excellent electrical and mechanical properties, and can produce less smoke and is halogen-free when exposed to fire, reducing harm to the human body and the environment.

The development and application of silane cross-linked low-smoke halogen-free polyolefin insulation materials have made this type of material mainly used in wiring in China.

Foreign products can also be used in solar energy, automotive wires and even nuclear power plant cables。Silane cross-linking technology provides an effective cross-linking method that can be cross-linked under warm water or steam conditions, or naturally cross-linked at room temperature, which makes the production process more flexible